Nanowires plated on nanoparticles

ABSTRACT

In some examples, a system comprises a set of nanoparticles and a set of nanowires extending from the set of nanoparticles.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims priority to the following U.S.provisional patent applications filed on Apr. 8, 2019, all of which arehereby incorporated herein by reference in their entireties: App. Nos.62/830,944; 62/830,989; 62/831,000; 62/831,016; and 62/831,065.

BACKGROUND

Many devices include multiple components that are attached to eachother. Such attached components can be found in virtually any type ofdevice or apparatus, including electronics, motor vehicles, furniture,clothing and apparel, and the like. The components are often attached toeach other using an adhesive (e.g., glue), nails, screws, or other suchmaterials.

SUMMARY

In some examples, a system comprises a set of nanoparticles and a set ofnanowires extending from the set of nanoparticles.

In some examples, a system comprises a first surface, a first set ofnanoparticles coupled to the first surface, and a first set of nanowiresextending from the first set of nanoparticles. The system also comprisesa second surface, a second set of nanoparticles coupled to the secondsurface, and a second set of nanowires extending from the second set ofnanoparticles. The first and second sets of nanowires are fused to eachother.

In some examples, a method comprises depositing a set of nanoparticleson a surface and positioning a template over the set of nanoparticles,the template having a plurality of orifices extending perpendicular tothe surface. The method also comprises electroplating the set ofnanoparticles to cause a set of nanowires to extend from the set ofnanoparticles and through the plurality of orifices. The method furthercomprises removing the template from the surface.

BRIEF DESCRIPTION OF THE DRAWINGS

For a detailed description of various examples, reference will now bemade to the accompanying drawings in which:

FIGS. 1A1-1E2 depict a process flow for plating a set of nanowires to aset of nanoparticles, in accordance with various examples;

FIG. 2 depicts a close-up, top-down view of a set of nanoparticles onwhich a set of nanowires may be plated, in accordance with variousexamples;

FIGS. 3A1-3D2 depict another process flow for plating a set of nanowiresto a set of nanoparticles, in accordance with various examples;

FIGS. 4A1-4F depict a process flow for coupling multiple componentsusing nanowires plated on nanoparticles, in accordance with variousexamples;

FIG. 5 depicts a structure resulting from the process flow of FIGS.4A1-4F, in accordance with various examples;

FIG. 6 depicts another structure resulting from the process flow ofFIGS. 4A1-4F, in accordance with various examples;

FIG. 7 depicts another structure resulting from the process flow ofFIGS. 4A1-4F, in accordance with various examples.

FIG. 8 depicts another structure resulting from a modified version ofthe process flow of FIGS. 4A1-4F, in accordance with various examples.

FIGS. 9A1-9H depict a process flow for performing a die attach in asemiconductor package using nanowires plated on nanoparticles, inaccordance with various examples;

FIGS. 10A1-10H depict another process flow for performing a die attachin a semiconductor package using nanowires plated on nanoparticles, inaccordance with various examples;

FIG. 11A depicts a semiconductor package having a heatsink comprising aset of nanowires plated on a set of nanoparticles, in accordance withvarious examples;

FIG. 11B depicts a top-down view of the semiconductor package of FIG.11A, in accordance with various examples;

FIG. 12A depicts a semiconductor package comprising nanowires plated onnanoparticles as interconnects, in accordance with various examples; and

FIG. 12B depicts another semiconductor package comprising nanowiresplated on nanoparticles as interconnects, in accordance with variousexamples.

DETAILED DESCRIPTION

As explained above, a variety of materials are conventionally used toattach multiple components together. Such materials have associateddisadvantages relating to adhesion strength, cost, mechanical stability,electrical properties, etc. For example, multiple components may beattached to each other in a semiconductor package using solder, whichhas electromigration problems introduced by the presence of differentmetals abutting each other. In some cases, multiple components may beattached to each other in a semiconductor package using nanoparticles,but the nanoparticle-to-nanoparticle coupling is generally weak andmechanically unstable. Glue may be used to form a stronger and morestable mechanical connection, but glue has poor thermal and electricalconductivity. A variety of other techniques may be used in thesemiconductor context, each entailing some combination of tedium,excessive cost, excessive space, poor mechanical stability, poorelectrical and thermal conductivity, and numerous photolithographysteps. Other components, for example in automobiles, may be attached toeach other using screws, nuts, and bolts, but these materials occupyexcessive space and are tedious to implement. Similar problems existwith most, if not all, materials used to attach components to eachother.

This disclosure describes a novel technique for attaching two or morecomponents to each other, regardless of the context or particularapplication in which those components are deployed. The techniqueincludes the deposition and melting of a set of nanoparticles on thesurfaces of the components to be attached. The technique furtherincludes the plating of a set of nanowires on each set of nanoparticles.The sets of nanowires are then coupled to each other. Because thesurface area of a nanowire is significantly greater than the volume ofthe nanowire, the number of surface defects on the nanowire issignificant, thereby depressing the melting point of the nanowire.Because nanowires have significantly depressed melting points (e.g.,room temperature, such as 65 degrees to 80 degrees Fahrenheit, or up toaround 175 degrees Fahrenheit in some examples), pressing the nanowiresof one component against the nanowires of another component causes thenanowires to melt due to the ambient temperature and the pressureapplied. In this way, the nanowires of multiple components can simply bepressed together at room temperature to cause the components to melt andto be attached to each other. Relative to other techniques for couplingcomponents together, the nanowires provide strong adhesion, mechanicalstability, little or no electromigration, reduced tedium, and goodelectrical and thermal conductivity. In addition, the use ofnanoparticles to plate the nanowires provides additional mechanicalstability to the nanowires, preventing the nanowires from flaking off ofthe components to which they are attached.

Various examples for fabricating and deployingnanowire-plated-nanoparticles are now described with respect to thedrawings. Although these examples are primarily described in the contextof semiconductor devices, the nanowire-plated-nanoparticles describedherein may be deployed in any of a variety of applications and contexts,virtually without limitation. Any application in which two or morecomponents are attached to each other may find benefit from the use ofthe nanowire-plated-nanoparticles described herein.

FIGS. 1A1-1E2 depict a process flow for plating a set of nanowires to aset of nanoparticles, in accordance with various examples. The processflow begins in FIG. 1A1 with the deposition of a set of nanoparticles104 on a surface (the drawings depict three sets of nanoparticles 104 toillustrate the fact that, in at least some applications, the processdescribed below can be applied in multiple instances simultaneously). Insome examples, such as the one depicted in FIG. 1A1, the surfacecomprises a metal layer (e.g., a solid metal layer of any desiredthickness) positioned on a semiconductor wafer 100, for example a metallayer 102. The remainder of the discussion of FIGS. 1A1-1E2 assumes thatthe surface includes the metal layer 102. In other examples, asdescribed in greater detail below, the surface comprises a semiconductorwafer, such as the wafer 100. In examples, other types of surfacesbesides the metal layer 102 and the wafer 100 may be used. In addition,components other than semiconductor wafers may be used, for example innon-semiconductor contexts.

In some examples, the metals in the set of nanoparticles 104 and themetal layer 102 are identical (e.g., copper, titanium, ortitanium-tungsten). In other examples, the metals in the set ofnanoparticles are different. For instance, in some examples, the set ofnanoparticles 104 comprises titanium or titanium-tungsten, and the metallayer 102 comprises copper. In some examples, the set of nanoparticles104 comprises nickel palladium, and the metal layer 102 comprisescopper. Any of a variety of metals may be used, depending on variousfactors including cost, electromigration between metals, availability,etc.

In some examples, the set of nanoparticles 104 is deposited on the metallayer 102 using a printing technique, for example an additivemanufacturing technique. In some examples, the set of nanoparticles 104is electroplated onto the metal layer 102. In some examples, the set ofnanoparticles 104 is deposited using a sputtering technique. Othertechniques are contemplated and included in the scope of thisdisclosure.

In some examples, the set of nanoparticles 104 has a thickness rangingfrom 100 nanometers (nm) to 100 microns, with a thicker set ofnanoparticles 104 resulting in a more mechanically stablenanoparticle-nanowire structure. In some examples, the set ofnanoparticles 104 has a uniform thickness throughout its length andwidth, and in other examples, the set of nanoparticles 104 has anon-uniform thickness throughout its length and width. The remainingdimensions of the set of nanoparticles 104 may be chosen as desired. Insome examples, each nanoparticle in the set of nanoparticles 104 isgenerally spherical and has a diameter ranging from approximately 0.5microns to 1.5 microns. The specific physical parameters of the set ofnanoparticles 104 and the individual nanoparticles within the set ofnanoparticles 104 may vary, and all such variations are encompassedwithin the scope of this disclosure. The length, width, and thickness ofthe metal layer 102 may be chosen as desired. Similarly, the number ofmetal layers 102 (and attendant sets of nanoparticles 104) may be chosenas desired, with certain applications benefiting from more and otherapplications benefiting from fewer.

After the set of nanoparticles 104 is positioned on the metal layer 102,the set of nanoparticles 104 is melted to cause the nanoparticles in theset of nanoparticles 104 to diffuse into the metal layer 102. Anysuitable technique may be used to melt the set of nanoparticles 104, forexample a laser or any other heat source. The diameter of thenanoparticles in the set of nanoparticles 104, as well as the thicknessof the set of nanoparticles 104, may determine the melting point of theset of nanoparticles 104. In some examples, a nanoparticle diameter ofapproximately 1 micron and a thickness for the set of nanoparticles 104of approximately 100 nm may result in a melting point of approximately200 degrees Fahrenheit, although the specific number can vary based on avariety of factors (e.g., metal used, physical parameters of thenanoparticles and the set of nanoparticles 104). FIG. 1A2 shows atop-down view of the structure of FIG. 1A1.

After the set of nanoparticles 104 has been diffused into the metallayer 102, nanowires may be plated onto the set of nanoparticles 104.Photolithography techniques may be used to produce a photoresist 106 inthe pattern shown in FIG. 1B1, abutting the set of nanoparticles 104.For example, a photoresist may be applied, exposed using a suitablypatterned mask, and developed to produce the photoresist 106. In someexamples, a top surface of the photoresist 106 is flush or at leastapproximately flush with the top surface of the set of nanoparticles104. For example, if the thickness of the set of nanoparticles 104 isnon-uniform, the set of nanoparticles 104 will have an uneven topsurface and thus the top surface of the photoresist 106 is approximatelyflush with the top surface of the set of nanoparticles 104. By“approximately flush,” it is meant that the top surface of thephotoresist 106 is at or above the lowest point of the set ofnanoparticles 104 and at or below the highest point of the set ofnanoparticles 104, although the scope of this disclosure is not limitedas such.

In FIG. 1C1, a template 108 is coupled to the photoresist 106 and isusable to plate nanowires onto the set of nanoparticles 104. Thistemplate may comprise, for example, a TEFLON® (polytetrafluoroethylene)filter. In other examples, the template 108 comprises plastic. In someexamples, the template 108 comprises any suitable type of metal (e.g.,anodized aluminum or nickel). The template 108 rests on the photoresist106 and on the set of nanoparticles 104 as shown. The photoresist 106 isnot needed to mechanically support the template 108; because the set ofnanoparticles 104 is negligibly thin in actual implementation asdescribed above, the template 108 may simultaneously rest on the wafer100 and the set of nanoparticles 104 in the absence of the photoresist106, as described below (with the thicknesses of the metal layer 102 andthe photoresist 106 being exaggerated in the drawings for clarity).Rather, the photoresist 106 is present in some examples to adhere to thetemplate 108 in the event that the template 108 is composed of amaterial that does not adhere firmly to the wafer 100. If the template108 is composed of a material that adheres firmly to the wafer 100, thephotoresist 106 may be omitted.

Referring still to FIG. 1C1, the template 108 includes groups oforifices 109 extending perpendicularly to the metal layer 102 (or, inthe absence of the metal layer 102, perpendicularly to the wafer 100).Each group of orifices 109 is positioned above a different set ofnanoparticles 104, as shown. FIG. 1C2 depicts a top-down view of thestructure of FIG. 1C1. As FIG. 1D1 depicts, an electroplating process isthen performed, whereby a set of nanowires 110 is plated onto the set ofnanoparticles 104. Any suitable metal may be used when plating the setof nanowires 110. In some examples, gold is used to plate the set ofnanowires 110. In some examples, copper is used to plate the set ofnanowires 110. In some examples, titanium is used to plate the set ofnanowires 110. In some examples, tungsten is used to plate the set ofnanowires 110. In examples, the various nanowires described in thisdisclosure are metallic nanowires and the various nanoparticlesdescribed in this disclosure are metallic nanoparticles.

Still referring to FIG. 1D1, in some examples, the orifices 109 in thetemplate 108 are sized appropriately to form wires at a nanoscale. Forexample, a nanowire in the set of nanowires 110 may have a length thatis at least twice its diameter. In some examples, a nanowire in the setof nanowires 110 has a length that is at least 10 times its diameter. Insome examples, a nanowire in the set of nanowires 110 has a length thatis at least 100 times its diameter. In some examples, a nanowire in theset of nanowires 110 has a length that is at least 1000 times itsdiameter. In some examples, a nanowire in the set of nanowires 110 has adiameter ranging from 0.5 microns to 1.5 microns. In some examples, ananowire in the set of nanowires 110 has a diameter of 1 micron or nomore than 1 micron. In some examples, a nanowire in the set of nanowires110 has a length of at least 2 microns. In other examples, otherdiameters and length-to-diameter ratios of nanowires are contemplated,and all such measurements and combinations fall within the scope of thisdisclosure. The orifices 109 may have dimensions similar to the exampledimensions given for the nanowires above. FIG. 1D2 depicts a top-downview of the structure of FIG. 1D1.

The various dimensions described for the nanowires and nanoparticles arenot mere design choices. Rather, adjusting each dimension to be largeror smaller may provide specific functional benefits. For example,adjusting a nanowire length to be greater and/or a nanowire diameter tobe smaller, such that the ratio of length to diameter increases, mayincrease the surface area of the nanowire. Increasing the surface areaof the nanowire increases the number of defects present, therebydepressing the melting point of the nanowire and making it easier tofuse the nanowire to other materials without requiring high temperatureor pressure.

In FIG. 1E1, the photoresist 106 and the template 108 are removed. Forexample, the photoresist 106 may be removed using a resist strippingtechnique (e.g., wet or dry etching). The template 108 may be removed,for example, using the same resist stripping technique as used for thephotoresist 106 (in the case of a TEFLON® or plastic template 108) orusing a specific metal etch corresponding to the metal(s) of which thetemplate 108 is composed. Removal of the photoresist 106 and thetemplate 108 leaves the structure shown in FIG. 1E1, which includes thewafer 100, metal layers 102, sets of nanoparticles 104, and sets ofnanowires 110 plated on the sets of nanoparticles 104. FIG. 1E2 depictsa top-down view of the structure of FIG. 1E1. FIG. 2 depicts a detailedview of the set of nanoparticles 104.

As explained above, a set of nanoparticles may be deposited on virtuallyany surface. In FIGS. 1A1-1E2 and 2, the set of nanoparticles 104 isdeposited on a metal layer 102. In other examples, such as in FIGS.3A1-3D2 and 4A-4B, the set of nanoparticles 104 is deposited directly onthe wafer 100 (although, again, surfaces other than the wafer 100 may beused). In particular, FIGS. 3A1-3D2 depict another process flow forplating a set of nanowires to a set of nanoparticles, in accordance withvarious examples. The process flow of FIGS. 3A1-3D2 is nearly identicalto the process flow of FIGS. 1A1-1E2, except that the metal layer 102and the photoresist 106 are both omitted. As explained above, thephotoresist 106 may be omitted if the template 108 is composed of amaterial that adheres firmly to the wafer 100 (or other surface). Inthis case, the template 108 rests on the wafer 100 and on the set ofnanoparticles 104. As explained above, the template 108 is able to restsimultaneously on the wafer 100 and the set of nanoparticles 104 becausethe thickness of the set of nanoparticles 104 is virtually negligible.In FIGS. 3B1 and 3C1, however, the thickness of the set of nanoparticles104 is exaggerated to provide clarity regarding the structure beingfabricated by the process flow of FIGS. 3A1-3D2, and for this reason,the template 108 is shown as not making direct contact with the wafer100. In actual implementation, however, the template 108 may make directcontact with the wafer 100.

FIGS. 4A1-4F depict a process flow for coupling multiple componentsusing nanowires plated on nanoparticles, in accordance with variousexamples. In particular, FIG. 4A1 depicts a component 500. The component500 may be any component in any system, such as a semiconductor wafer,an automotive part, a consumer electronic device, a household appliance,an article of clothing or jewelry, etc. Metal layers 502, in someexamples, may be similar to the metal layers 102 described above interms of composition, size, shape, and/or fabrication, and arepositioned on a surface of the component 500. Sets of nanoparticles 504,in some examples, may be similar to the sets of nanoparticles 104described above in terms of composition, size, shape, and/orfabrication, and are positioned on the metal layers 102 as shown. FIG.4A2 depicts a top-down view of the structure of FIG. 4A1. As shown inFIG. 4B1, sets of nanowires 510 are plated on the sets of nanoparticles504 (for brevity, photolithography steps are not shown), with the setsof nanowires 510 being similar to the sets of nanowires 110 in terms ofcomposition, size, and fabrication. FIG. 4B2 shows a top-down view ofthe structure of FIG. 4B1.

In FIG. 4C1, a pair of components 550, 552 is depicted, where thecomponents 550, 552 are any components in any system, such as a packagelead frame, an automotive part, a consumer electronic device, ahousehold appliance, an article of clothing or jewelry, etc. Thecomponents 550, 552 may be identical or different in composition, size,shape, or fabrication. Two components 550, 552 are depicted toillustrate the adaptability of the nanowire-plated-nanoparticletechnology described herein to a variety of situations, such as thecoupling of a single component to multiple other components using thetechnology described herein. FIG. 4C2 depicts a top-down view of thestructure of FIG. 4C1. In FIG. 4D1, metal layers 554 are formed on thecomponent 550, and metal layer 560 is formed on the component 552. Themetal layers 554, 560 may be similar to the metal layers 102 describedabove in terms of composition, size, shape, and/or fabrication. Sets ofnanoparticles 556 are positioned on the metal layers 554, and the set ofnanoparticles 558 is positioned on the metal layer 560. The sets ofnanoparticles 556, 558 may be similar to the sets of nanoparticles 104described above in terms of composition, size, shape, and/orfabrication. FIG. 4D2 depicts a top-down view of the structure of FIG.4D1. In FIG. 4E1, sets of nanowires 562 are plated on the sets ofnanoparticles 556 (again, the photolithography steps being omitted fromillustration for brevity), and a set of nanowires 564 is plated on theset of nanoparticles 558. The sets of nanowires 562, 564 may be similarto the sets of nanowires 110 in terms of composition, size, shape, andfabrication. FIG. 4E2 depicts a top-down view of the structure of FIG.4E1.

In FIG. 4F, the component 550, with its corresponding metal layers, setsof nanoparticles, and sets of nanowires, is coupled to the components550, 552, with their corresponding metal layers, sets of nanoparticles,and sets of nanowires. In particular, the sets of nanowires 510 arealigned with the sets of nanowires 562, 564 and are subsequently pressedtogether. When the sets of nanowires 510 are pressed against the sets ofnanowires 562, 564, the nanowires fuse together. In general, any twonanowires may fuse together at any point or points of contact. Inexamples, the fusion of two nanowires generally occurs along the lengthsof the nanowires, as described below. A fusion along the lengths of twonanowires may be complete, meaning that the entire lengths of the twonanowires are fused together. In some examples, the fusion along thelengths of two nanowires may be incomplete, meaning that only portionsof the lengths of the two nanowires are fused together, and theseportions may be contiguous or separate. In some examples, a pair ofnanowires may fuse together using a distal end of one of the nanowiresin the pair. In some examples, three or more nanowires may bunchtogether and couple together along their lengths or in another suitablemanner. In some examples, one or more nanowires may wrap around one ormore other nanowires. Any and all such manners of fusion arecontemplated and included within the scope of this disclosure. Fusionbetween nanowires may occur as a result of nanowires contacting eachother with a minimum amount of pressure and/or temperature. For example,at room temperature, pressures greater than 100 MPa are sufficient tocause fusion. Temperatures of approximately 175 degrees Fahrenheit aresufficient to cause fusion without any additional pressure being added.Other combinations of pressure and temperature sufficient to causemelting and subsequent fusion of nanowires also may be used.

FIGS. 5 and 6 depict additional structures resulting from the processflow of FIGS. 4A1-4F, in accordance with various examples. In FIG. 5,one component 500 couples to another component 600 usingnanowire-plated-nanoparticles. The structure of FIG. 5 differs from thatof FIG. 4F in that the structure of FIG. 5 comprises two componentscoupling to each other instead of one component coupling to two othercomponents. In this way, FIGS. 4F and 5 depict the adaptability of thenovel techniques herein to a variety of applications. In some examples,the components 500, 600 are semiconductor wafers (or post-singulationdies). Metal layers 502 are coupled to the component 500, with sets ofnanoparticles 504 positioned on the metal layers 502 and sets ofnanowires 510 plated on the sets of nanoparticles 504. Metal layers 602are coupled to the component 600, with sets of nanoparticles 604positioned on the metal layers 602 and sets of nanowires 606 plated onthe sets of nanoparticles 604. The metal layers, sets of nanoparticles,and sets of nanowires depicted in FIG. 6 may be similar in composition,size, shape, and/or fabrication to the metal layers, sets ofnanoparticles, and sets of nanowires described above.

In FIG. 6, a component 708 couples to a component 700 usingnanowire-plated-nanoparticles. Specifically, metal layers 710 arepositioned on the component 708, with sets of nanoparticles 712positioned on the metal layers 710. Sets of nanowires 714 are plated onthe sets of nanoparticles 712. Similarly, metal layers 702 arepositioned on the component 700, with sets of nanoparticles 704positioned on the metal layers 702. Sets of nanowires 706 are plated onthe sets of nanoparticles 704. The metal layers, sets of nanoparticles,and sets of nanowires depicted in FIG. 6 may be similar in composition,size, shape, and/or fabrication to the metal layers, sets ofnanoparticles, and sets of nanowires described above. In FIG. 6, thecomponents 708, 700 may be any components of any system, but in at leastsome examples, the component 708 comprises a passive electricalcomponent (e.g., a resistor, capacitor, inductor, sensor) and thecomponent 700 comprises a semiconductor wafer (or post-singulation die).

The examples of FIGS. 4A1-4F, 5, and 6 include metal layers on whichsets of nanoparticles are positioned. Such metal layers may be formed asdescribed above with respect to FIGS. 1A1 -1E2 and 2. However, asdescribed above with respect to FIGS. 3A1-3D2, in some examples, a metallayer may be omitted and a set of nanoparticles (along with nanowireplating) may be formed directly on the surface of the component.Accordingly, although the examples of FIGS. 4A1-4F, 5, and 6 includemetal layers, this disclosure contemplates examples that are identicalto those of FIGS. 4A1-4F, 5, and 6 but without the use of the metallayers depicted in those drawings. Thus, in such examples, the sets ofnanoparticles may be positioned directly on the component surface, andsets of nanowires may be plated on the sets of nanoparticles.

FIG. 7 depicts another structure resulting in part from the process flowof FIGS. 4A1-4F, in accordance with various examples. Specifically, inFIG. 7, a semiconductor package is coupled to another component, such asa printed circuit board (e.g., PCB), usingnanowire-plated-nanoparticles. FIG. 7 depicts a component 800 (e.g.,PCB) having metal layers 802 formed therein. In alternative examples,the metal layers 802 are formed on, instead of in, the component 800.Sets of nanoparticles 804 are positioned on the metal layers 802. Setsof nanowires 806 are plated on the sets of nanoparticles 804. Inaddition, FIG. 7 depicts a semiconductor package 808 comprising a die810 mounted on a die pad 814 a using a die attach 812 (e.g., solder).The die 810 is communicably coupled with package leads 814 b via bondwires 816. (Various alternative die and lead frame configurations withinthe semiconductor package 808, e.g., flip chip, stacked die, clipped,etc., are contemplated and included within the scope of this disclosure,and particularly within the scope of the example of FIG. 7.) Sets ofnanoparticles 818 are formed on the die pad 814 a and package leads 814b, and sets of nanowires 820 are plated on the sets of nanoparticles818. The sets of nanowires 820, 806 are pressed together, thereby fusingthe nanowires together as described above and causing the package 808 toadhere to the component 800. In FIG. 7, the metal layers, sets ofnanoparticles, and sets of nanowires may have the same composition,size, shape, and/or fabrication as the metal layers, sets ofnanoparticles, and sets of nanowires described above.

Many of the examples described above include two or more componentscoupling to each other using nanowire-plated-nanoparticles, where thenanowires and nanoparticles are present on each of the components beingcoupled. The scope of this disclosure is not limited, however, toexamples in which all components being coupled have nanoparticles andnanowires positioned on them. Rather, the scope of this disclosureincludes components that couple together usingnanowire-plated-nanoparticles where fewer than all of the componentsbeing coupled have nanowires and nanoparticles positioned thereupon.FIG. 8 depicts such a structure, in accordance with various examples. InFIG. 8, components 900 and 904 couple to each other using thenanowire-plated-nanoparticle technology described herein. A metal layer902 is positioned on the component 900, and a metal layer 906 ispositioned on the component 904. As explained above, such metal layersare optional and in some examples may be excluded. The metal layer 906has positioned thereupon a set of nanoparticles 908, and a set ofnanowires 910 is plated on the set of nanoparticles 908. When pressedagainst the metal layer 902, the set of nanowires 910 fuses to the metallayer 902. The manner in which the set of nanowires 910 fuses to themetal layer 902 is similar to the manner in which nanowires fusetogether as described above, e.g., the set of nanowires 910 melts whenthe appropriate combination of pressure and temperature is applied, thuscausing the set of nanowires 910 to fuse to the metal layer 902. Thistechnique may be used to couple any plurality of components together, asdesired. In FIG. 8, the metal layers, sets of nanoparticles, and sets ofnanowires may have the same composition, size, shape, and/or fabricationas the metal layers, sets of nanoparticles, and sets of nanowiresdescribed above.

As explained above, FIG. 7 depicts the use ofnanowire-plated-nanoparticles on an exterior of a component, such as asemiconductor package, to couple the component to another component. Thenanowire-plated-nanoparticles, however, also may be used within asemiconductor package, for example to act as a die attach that couples asemiconductor die to a die pad or other component. FIGS. 9A1-9H depict aprocess flow for performing a die attach in a semiconductor packageusing nanowires plated on nanoparticles, in accordance with variousexamples. In FIG. 9A1, a component 1000, such as a semiconductor die, isprovided, and in FIG. 9B1, a set of nanoparticles 1002 is positioned onthe component 1000. FIGS. 9A2 and 9B2 depict top-down and bottom-upviews of the structures of FIGS. 9A1 and 9B1, respectively. In FIG. 9C1,a set of nanowires 1004 is plated on the set of nanoparticles 1002.(Note that the orientation of the structure in FIG. 9C1 is merely toassist in understanding the assembly of structures described below.Assembly of the structure of FIG. 9C1 (e.g., including electroplating)may be performed with the structure in a different orientation (e.g.,rotated 180 degrees).) In some examples, a metal layer, such as thosedescribed above, may be included between the component 1000 and the setof nanoparticles 1002, although in FIGS. 9A1-9H, such metal layers areexcluded. FIG. 9C2 depicts a bottom-up view of the structure of FIG.9C1. In FIG. 9D1, a component 1010, such as a lead frame die pad, isprovided, and in FIG. 9E1, a set of nanoparticles 1014 is positioned onthe component 1010. FIGS. 9D2 and 9E2 depict top-down views of thestructures of FIGS. 9D1 and 9E1, respectively. In FIG. 9F1, a set ofnanowires 1016 is plated on the set of nanoparticles 1014. FIG. 9F2depicts a top-down view of the structure of FIG. 9F1. In FIG. 9G, thesets of nanowires 1004, 1016 are pressed together in the mannerdescribed above, thereby causing the nanowires to fuse together, also asdescribed above. The structure of FIG. 9G may then be completed by,e.g., the application of wirebonds and a mold compound 120 to cover thestructure, as FIG. 9H depicts. In FIG. 9H, bond wires 1018 couple thecomponent 1000 to leads 1011, while the component 1000 is attached tothe component 1010 using nanowire-plated-nanoparticles. In FIGS. 9A1-9H,the sets of nanoparticles and sets of nanowires may have the samecomposition, size, shape, and/or fabrication as the sets ofnanoparticles, and sets of nanowires described above.

As described above, when multiple components are coupled together,nanowire-plated-nanoparticles are not necessarily present on allcomponents being coupled. FIGS. 10A1-10H depict a process flow similarto that of FIGS. 9A1-9H, but with nanowire-plated-nanoparticles presenton only one of the two components being coupled together. In FIG. 10A1,a component 1000, such as a semiconductor wafer, is provided, and inFIG. 10E31, a set of nanoparticles 1002 is positioned on the component1000. FIGS. 10A2 and 10132 depict top-down and bottom-up views of thestructures of FIGS. 10A1 and 10E31, respectively. In FIG. 10C1, a set ofnanowires 1004 is plated on the set of nanoparticles 1002. In someexamples, a metal layer may be included between the component 1000 andthe set of nanoparticles 1002, although in FIGS. 10A1-10H, such metallayers are excluded. FIG. 10C2 depicts a bottom-up view of the structureof FIG. 10C1. In FIG. 10D1, the component 1000, which may be asemiconductor wafer, is singulated into, e.g., a plurality ofsemiconductor dies 1000. FIG. 10D2 depicts a bottom-up view of thestructure of FIG. 10D1. In FIG. 10E1, a component 1010, such as a leadframe die pad, is provided, and in FIG. 10F, one of the singulatedcomponents of FIG. 10D1 is positioned on the component 1010. FIG. 10E2depicts a top-down view of the structure of FIG. 10E1. In FIG. 10G,pressure and/or temperature is applied to the component 1000, therebycausing the set of nanowires 1004 to melt and fuse to the component 1010due to the appropriate combination of heat and pressure. In FIG. 10H,bond wires 1018 couple the component 1000 to leads 1011, while thecomponent 1000 is attached to the component 1010 usingnanowire-plated-nanoparticles. A mold compound 1020 covers the structureto form a semiconductor package. In FIGS. 10A1-10H, the sets ofnanoparticles and sets of nanowires may have the same composition, size,shape, and/or fabrication as the sets of nanoparticles, and sets ofnanowires described above.

As explained above, nanowires are able to melt at low temperatures(e.g., room temperature) due to their high surface area-to-volume ratio.This degree of surface area exposure provides another benefit in theefficient release of heat. Accordingly, nanowires may be used as heatsinks in appropriate contexts. For example, FIG. 11A depicts asemiconductor package 1200 having a heatsink comprising a set ofnanowires plated on a set of nanoparticles, in accordance with variousexamples. Specifically, package 1200 includes the structure of FIG. 4F,including the component (e.g., semiconductor die) 500, components 550,552, metal layers 502, 554, 560, sets of nanoparticles 504, 556, 558,and sets of nanowires 562, 564, 510 coupled as shown and as describedabove with respect to FIG. 4F. The backside (non-active) surface of thecomponent 500 is exposed to a top surface of the package 1200 such thatthe backside surface of the component 500 is not covered by a moldcompound or epoxy. The component 500 has an optional metal layer 1202coupled to it, and a set of nanoparticles 1204 is positioned on themetal layer 1202. A set of nanowires 1206 is plated on the set ofnanoparticles 1204. Heat generated from within the package 1200, forexample by the component 500, passes through the metal layer 1202, theset of nanoparticles 1204, and the set of nanowires 1206, being radiatedaway from the package 1200 by the set of nanowires 1206. In FIG. 11A,the metal layers, sets of nanoparticles and sets of nanowires may havethe same composition, size, shape, and/or fabrication as the metallayers, sets of nanoparticles, and sets of nanowires described above.FIG. 11B depicts a top-down view of the structure of FIG. 11A.

The nanowire-plated-nanoparticle technology described herein efficientlyconducts heat and electricity, making it suitable for applications inwhich improved heat dissipation is needed (e.g., as in FIGS. 11A and11B) and/or in which wide temperature fluctuations have a deleteriousimpact on the mechanical integrity of a device. For example, widetemperature fluctuations can cause cracking and delamination of bondwire interconnect layers and/or of die attach layers and/or substratebond layers, all of which are frequently solder-based layers.Accordingly, FIGS. 12A and 12B depict semiconductor packages comprisingnanowire-plated-nanoparticles as interconnects that facilitate thecoupling of bond wires, dies, and substrates. Thesenanowire-plated-nanoparticle interconnects promote the efficientelimination of heat from the package and, in addition, they resistcracking and delamination when subjected to wide temperature swings.

In FIG. 12A, a semiconductor package 1300 comprises a pair ofsemiconductor dies 1302, 1304, although any number of dies may be used.Busbars 1306, 1308 couple to the dies 1302, 1304, respectively, usingnanowire-plated-nanoparticles. In particular, the busbar 1306 has a setof nanoparticles 1310 coupled thereto, with a set of nanowires 1318plated to the set of nanoparticles 1310. The set of nanowires 1318 isfused to another set of nanowires 1320, which is plated on a set ofnanoparticles 1312, which is positioned on a top surface of the die1302. Similarly, busbar 1308 has a set of nanoparticles 1314 coupledthereto, with a set of nanowires 1322 plated to the set of nanoparticles1314. The set of nanowires 1322 is fused to another set of nanowires1324, which is plated to a set of nanoparticles 1316, which ispositioned on a top surface of the die 1304. In addition, a set ofnanoparticles 1326 is positioned on the die 1302, and a set of nanowires1328 is plated on the set of nanoparticles 1326. Similarly, a set ofnanoparticles 1332 is positioned on the die 1304, and a set of nanowires1334 is plated on the set of nanoparticles 1332. The sets of nanowires1328, 1334 are fused to a set of nanowires 1330, which are plated on aset of nanoparticles 1336, and the set of nanoparticles 1336 ispositioned on a metal layer 1338. The metal layer 1338, in turn, iscoupled to a substrate (e.g., a ceramic substrate) layer 1340.

Still referring to FIG. 12A, a metal layer 1342 couples to the substratelayer 1340, with a set of nanoparticles 1344 positioned on the metallayer 1342. A set of nanowires 1346 is plated on the set ofnanoparticles 1344. The set of nanowires 1346 is fused to a set ofnanowires 1348. The set of nanowires 1348 is plated on a set ofnanoparticles 1350, which is positioned on a metal layer 1352. A set ofnanoparticles 1354 is positioned on the metal layer 1352, and a set ofnanowires 1356 is plated on the set of nanoparticles 1354. The set ofnanowires 1356 is exposed to an exterior of the package 1300. The set ofnanowires 1356 functions as a heat sink. In operation, data signals areprovided to and from the dies 1302, 1304 via the busbars 1306, 1308. Thebusbars 1306, 1308 may couple to any other electronic device and, thus,the ends of the busbars 1306, 1308 opposite the dies 1302, 1304 areshown as being unconnected to another electronic device (agnostic toother possible electronic device connections). The structures betweenthe dies 1302, 1304 and the set of nanowires 1356 transfer heat awayfrom the dies 1302, 1304, with the set of nanowires 1356 radiating theheat away from the package 1300.

FIG. 12B depicts a structure that is similar to that of FIG. 12A, butwithout the substrate (e.g., ceramic) layer 1340 and the associatedmetal layers 1338, 1342, sets of nanoparticles 1336, 1344, and sets ofnanowires 1330, 1346. In FIG. 12B, a semiconductor package 1400comprises a pair of semiconductor dies 1402, 1404, although any numberof dies may be used. Busbars 1406, 1408 couple to the dies 1402, 1404,respectively, using nanowire-plated-nanoparticles. In particular, thebusbar 1406 has a set of nanoparticles 1410 coupled thereto, with a setof nanowires 1418 plated to the set of nanoparticles 1410. The set ofnanowires 1418 is fused to another set of nanowires 1420, which isplated on a set of nanoparticles 1414, which is positioned on a topsurface of the die 1402. Similarly, busbar 1408 has a set ofnanoparticles 1412 coupled thereto, with a set of nanowires 1422 platedto the set of nanoparticles 1412. The set of nanowires 1422 is fused toanother set of nanowires 1424, which is plated to a set of nanoparticles1416, which is positioned on a top surface of the die 1404. In addition,a set of nanoparticles 1426 is positioned on the die 1402, and a set ofnanowires 1430 is plated on the set of nanoparticles 1426. Similarly, aset of nanoparticles 1428 is positioned on the die 1404, and a set ofnanowires 1432 is plated on the set of nanoparticles 1428. The sets ofnanowires 1430, 1432 are fused to a set of nanowires 1434, which areplated on a set of nanoparticles 1436, and the set of nanoparticles 1436is positioned on a metal layer 1438. The metal layer 1438, in turn, hasa set of nanoparticles 1440 positioned thereupon, and a set of nanowires1442 is plated on the set of nanoparticles 1440. The set of nanowires1442 is exposed to an exterior of the package 1400 and functions as aheat sink.

In operation, data signals are provided to and from the dies 1402, 1404via the busbars 1406, 1408. The busbars 1406, 1408 may couple to anyother electronic device and, thus, the ends of the busbars 1406, 1408opposite the dies 1402, 1404 are shown as being unconnected to (agnosticto) another electronic device. The structures between the dies 1402,1404 and the set of nanowires 1442 transfer heat away from the dies1402, 1404, with the set of nanowires 1442 radiating the heat away fromthe package 1400.

The above discussion is meant to be illustrative of the principles andvarious embodiments of the present disclosure. Numerous variations andmodifications will become apparent to those skilled in the art once theabove disclosure is fully appreciated. It is intended that the followingclaims be interpreted to embrace all such variations and modifications.Unless otherwise stated, “about,” “approximately,” or “substantially”preceding a value means +1- 10 percent of the stated value.

What is claimed is:
 1. A system, comprising: a set of nanoparticles; anda set of nanowires extending from the set of nanoparticles.
 2. Thesystem of claim 1, wherein at least one nanowire of the set of nanowireshas a length that is at least twice its diameter.
 3. The system of claim1, wherein at least one nanowire of the set of nanowires has a diameterof no more than 1 micron.
 4. The system of claim 1, wherein at least onenanowire of the set of nanowires has a length of at least 2 microns. 5.The system of claim 1, wherein the system comprises a metal layer onwhich the set of nanoparticles is positioned.
 6. The system of claim 1,wherein the set of nanoparticles comprises titanium and wherein the setof nanowires comprises gold.
 7. The system of claim 1, furthercomprising: a first surface on which the set of nanoparticles ispositioned; a second surface on which a second set of nanoparticles ispositioned; and a second set of nanowires extending from the second setof nanoparticles, wherein the set of nanowires and the second set ofnanowires couple to each other.
 8. The system of claim 1, furthercomprising a first surface on which the set of nanoparticles isdisposed, wherein the set of nanowires couples to a second surface, andwherein the first and second surfaces are positioned within a package.9. The system of claim 1, wherein the set of nanowires forms a heat sinkcoupled to a semiconductor die.
 10. The system of claim 1, furthercomprising: a die, the set of nanoparticles positioned on a firstsurface of the die; a busbar having a second set of nanoparticlespositioned thereupon, a second set of nanowires extending from thesecond set of nanoparticles, the second set of nanowires fused to theset nanowires; a substrate coupled to a first metal layer, the firstmetal layer coupled to the die by way of a third set of nanowires; and asecond metal layer coupled to the substrate, the second metal layercoupled to a third metal layer by way of a fourth set of nanowires,wherein the third metal layer comprises a fifth set of nanowirespositioned external to a package housing the die, the first metal layer,and the second metal layer.
 11. The system of claim 10, furthercomprising a third set of nanoparticles positioned on the die and afourth set of nanoparticles positioned on the first metal layer, thethird set of nanowires extending from the third set of nanoparticles anda sixth set of nanowires extending from the fourth set of nanoparticles,the third and sixth sets of nanowires fused to each other.
 12. Thesystem of claim 10, wherein the fifth set of nanowires and the fourthset of nanowires are positioned on opposing surfaces of the second metallayer.
 13. The system of claim 10, wherein the substrate comprises aceramic substrate.
 14. A system, comprising: a first surface; a firstset of nanoparticles coupled to the first surface; a first set ofnanowires extending from the first set of nanoparticles; a secondsurface; a second set of nanoparticles coupled to the second surface;and a second set of nanowires extending from the second set ofnanoparticles, the first and second sets of nanowires fused to eachother.
 15. The system of claim 14, wherein at least one of the first setof nanowires has length and diameter dimensions such that the at leastone of the first set of nanowires has a melting point between 65 and 175degrees Fahrenheit.
 16. The system of claim 14, wherein the firstsurface comprises a metal layer.
 17. The system of claim 14, wherein thefirst surface comprises a semiconductor.
 18. The system of claim 14,wherein at least one nanowire of the first set of nanowires has a lengththat is at least twice its diameter.
 19. The system of claim 14, whereinthe first surface, the first set of nanoparticles, and the first set ofnanowires are part of a semiconductor package, and wherein the secondsurface, the second set of nanoparticles, and the second set ofnanowires are part of a printed circuit board (PCB).
 20. The system ofclaim 14, wherein the first surface is that of a semiconductor die andthe second surface is that of a portion of a lead frame, and wherein thefirst and second surfaces are positioned within a semiconductor package.21. The system of claim 20, wherein the semiconductor die has a thirdsurface opposite the first surface, a third set of nanoparticlespositioned on the third surface, a third set of nanowires extending fromthe third set of nanoparticles, the third set of nanowires forming aheat sink exposed to an exterior of the semiconductor package.
 22. Thesystem of claim 14, wherein the first surface is that of a die, and thesecond surface is that of a busbar, the system further comprising: ametal layer coupled to the die by way of a third set of nanowires, themetal layer having a fourth set of nanowires positioned external to asemiconductor package housing the die.
 23. The system of claim 22,further comprising a third set of nanoparticles coupled to the die and afourth set of nanoparticles coupled to the metal layer, the third set ofnanowires coupled to the third and fourth sets of nanoparticles.
 24. Thesystem of claim 23, further comprising a fifth set of nanowires coupledto the die, wherein the third set of nanowires couples to the metallayer, the third and fifth sets of nanowires fused to each other.
 25. Amethod, comprising: depositing a set of nanoparticles on a surface;positioning a template over the set of nanoparticles, the templatehaving a plurality of orifices extending perpendicular to the surface;electroplating the set of nanoparticles to cause a set of nanowires toextend from the set of nanoparticles and through the plurality oforifices; and removing the template from the surface.
 26. The method ofclaim 25, further comprising patterning a photoresist on the surface,the photoresist abutting at least one nanoparticle of the set ofnanoparticles.
 27. The method of claim 26, further comprising abuttingthe template to the photoresist.
 28. The method of claim 25, wherein thesurface comprises a metal layer.
 29. The method of claim 28, wherein themetal layer and the set of nanoparticles are composed of a same metal.30. The method of claim 28, wherein the metal layer and the set ofnanoparticles are composed of different metals.